Test summary


Specimens are cut to a specified width. The seal is then peeled apart by holding the two “legs” of the barrier material in the jaws of a force testing stand set to separate at a constant speed between 200 - 300 mm/min. while the force and displacement are continuously measured. The peak force required to separate the seal is reported, this can also be expressed as peak force per width of the seal material in N/m. Depending upon the characteristics of the specimen, it may also be informative to report the average peeling force over the width of the seal as it separates, discarding the first 10% and the last 10% of the force Vs displacement curve.



Test apparatus


Tensile tester with grips and suitable range loadcell. This may be a vertical testing stand, or alternatively a horizontally oriented instrument



Preparation


Cut a sufficient quantity of strips from a representative sample to a width of 15 mm, 25 mm or 25.4 mm perpendicular to the seal, and 75mm plus the width of the seal in length. If required, condition the specimens in accordance with ASTM E 171



Test method


1. If required, condition the samples as per ASTM E 171.

2. Cut strips from the sample to the dimensions defined in the standard.

3. Clamp the ends of the sample strip into the jaws of the tensile tester with the seal perpendicular to the direction of movement, and equidistant between the fixed and moving jaws.

4. If required, support the tail of the test specimen (see the standard for an explanation).

5. Set the tensile tester in motion at a speed between 200 and 300 mm/min.

6. Record the tensile force and displacement as the seal is peeled apart.


Report

Record all details necessary to identify the sample including width and machine direction in relation to the direction of pull.

Report the speed of separation used by the tensile tester, and the method used to support the tail of the sample if appropriate.

Report the maximum tensile force in newtons encountered as the specimen is stressed to failure. This can also be expressed as force per unit width of the seal in newtons per metre.

Note the method of failure of the seal.

Depending upon the characteristics of the force Vs displacement curve, it may be informative to calculate the average force as the seal is separated, discarding the first and final 10% of the force Vs displacement curve.

MultiTest 1-i, hammadde ve bitmiş ürünlerin fiziksel özelliklerini test etmek için satın alınmıştır. 10N yük hücresi, çok hassas ve doğru bir okuma sağlayan iki ondalık basamağa kadar ölçüm yapabilir ve bu test çok iyi çalışır. MultiTest 1-i ihtiyaçlarımızı karşılar ve zamanla kullanıcı dostudur.

Adriana Jamesova,
Tuzlar Sağlık

Case study
T-peel sistemi ve sağlık ürünlerine uygun aksesuarlar
Tıbbi keselerdeki ısı sızdırmazlık mukavemetleri ile ilgili İngiliz Standardını karşılamak için Mecmesin, standarda uygunluğu açıkça göstermek için verileri grafik formatında gösteren operatör dostu bir sistem sağlamıştır.

David Dixon, Kalite Güvence Teknisyeni
Roket Medikal Plc

Case study
Isı yalıtımlı tıbbi kese T-soyma testi

Bir uzmanla konuşun

Bir ürün hakkında sorunuz mu var? Hemen Teknik Satış Mühendislerimizden birinden geri arama isteyin.